| Color: | |
|---|---|
| LVT TECHNICAL DATA SHEET | ||
| CHARACTERISTICS STANDARD GENERALLY USED-LVT | ||
| Thickness | - | 2.0mm-5.0mm |
| Density | - | 1.75-1.90g/cm³ |
| Wear layer | - | 0.2/0.3/0.4/0.5/0.55/0.7mm |
| Micro-scratch resistance | EN 16094 | MSR-B2 |
| Squareness | ISO24342:2007 | Max≤0.2mm |
| Straightness | ISO24342:2007 | Max≤0.2mm |
| Classification | ISO10582 | 23,31/33,42/34,43 |
| Dimensional stability | ISO23999:2021 | ≤0.12% |
| Curling | ISO23999:2021 | ≤1.2mm |
| Residual indentation | ISO24343-1:2007 | ≤0.10mm |
| Light stability | ISO105-B02:Method 3 | ≥6 |
| Fire resistance | EN13501-1 | Bf1-S1 |
| Slip resistance | DIN 51130 EN 13893 | R10 DS |
| Wear resistance | EN660-2 | Group P |
| Peel resistance | ISO24345:2006 | ≥75N/50mm |
| Determination of resistance to stains chemical resistance | ISO26987:2008 | No change in surface dulling,surface attack, or staining was detected |
| Flexibility | ISO24344:2008 Method A | There was no cracking shown in both directions when tested with a 50 mandreal |
| Castor chair | ISO4918:2016 | After 25000 cycles,test specimens no visible damage |
| Soluble heavy metal contents test | ASTMF963-11 | Free |
| Formaldehyde emissiom | EN717-1:2004 | Free |
| Utilization | - | Recyclable |
| LVT TECHNICAL DATA SHEET | ||
| CHARACTERISTICS STANDARD GENERALLY USED-LVT | ||
| Thickness | - | 2.0mm-5.0mm |
| Density | - | 1.75-1.90g/cm³ |
| Wear layer | - | 0.2/0.3/0.4/0.5/0.55/0.7mm |
| Micro-scratch resistance | EN 16094 | MSR-B2 |
| Squareness | ISO24342:2007 | Max≤0.2mm |
| Straightness | ISO24342:2007 | Max≤0.2mm |
| Classification | ISO10582 | 23,31/33,42/34,43 |
| Dimensional stability | ISO23999:2021 | ≤0.12% |
| Curling | ISO23999:2021 | ≤1.2mm |
| Residual indentation | ISO24343-1:2007 | ≤0.10mm |
| Light stability | ISO105-B02:Method 3 | ≥6 |
| Fire resistance | EN13501-1 | Bf1-S1 |
| Slip resistance | DIN 51130 EN 13893 | R10 DS |
| Wear resistance | EN660-2 | Group P |
| Peel resistance | ISO24345:2006 | ≥75N/50mm |
| Determination of resistance to stains chemical resistance | ISO26987:2008 | No change in surface dulling,surface attack, or staining was detected |
| Flexibility | ISO24344:2008 Method A | There was no cracking shown in both directions when tested with a 50 mandreal |
| Castor chair | ISO4918:2016 | After 25000 cycles,test specimens no visible damage |
| Soluble heavy metal contents test | ASTMF963-11 | Free |
| Formaldehyde emissiom | EN717-1:2004 | Free |
| Utilization | - | Recyclable |